模壓的制品 表面 有氣泡 怎么辦

玫70

<>我們用SMC  壓制汽車面罩 但是表面總是有氣泡，哪位高手 幫我分析一下原因</P>
<>先謝謝了</P>

sand

<>又是很trouble的問題?。?！</P>
<>可能產(chǎn)生的原因如下：</P>
<>一、材質(zhì)：</P>
<>1）Insufficient glass wet out with resin (dry glass)
玻璃纖維未能浸潤</P>
<>2）Foreign objects/contamination (film, flash, etc.) in or on the charge
有雜質(zhì)</P>
<>3）Wrinkles/pockets in discontinuous surface of SMC charge pattern
SMC表面不平整</P>
<>二、生產(chǎn)工藝：</P>
<>1）Adding small SMC pieces to charge pattern which trap air
小塊的SMC補(bǔ)片內(nèi)裹氣（布料不良）</P>
<>2）Insufficient pressure on SMC during cure cycle
固化時(shí)壓力不足</P>
<>3）Oven temperature heat-up rate too fast, especially in combination with a high moisture content part
烘箱加熱太快，特別是含水率偏高時(shí)</P>
<P>4）Improper charge patter (too large, rolled or folded)
充填不良</P>
<P>5）Vacuum too low; improper vacuum cycle
排氣動作不當(dāng)</P>
<P>6）Low cure time (under cure)
固化時(shí)間太短（未完全固化）</P>
<P>7）Press closure speed to fast (air trapped in laminate)
合模速度太快</P>
<P>三、模具：</P>
<P>1）Mold shear edge is too tight (not allowing air to bleed out)
模具間隙太?。o法排氣）</P>
<P>2）Tool Deflection
加工尺寸偏差</P>

[此貼子已經(jīng)被作者于2006-4-6 12:07:03編輯過]

玫70

<>翻譯成中文 如何 謝謝。</P>

sand

<>簡單翻譯了一下，湊或著看看吧。建議還是看英文，翻譯水平有限，有些意思中文很難表達(dá)。</P>

玫70

謝謝

丹晨子

在片材沒有熟化好的時(shí)候,既是粘度不大時(shí),也會造成產(chǎn)品表面有氣泡和氣孔產(chǎn)生.

letgo508

<>在片材暫時(shí)不好改的情況下,調(diào)整模壓工藝,主要在加料方式上調(diào)整看看.另外你的抽真空不?</P>

玫70

<B></B>
<>在片材暫時(shí)不好改的情況下,調(diào)整模壓工藝,主要在加料方式上調(diào)整看看.另外你的抽真空不?</P><>怎么抽真空啊 沒有接觸過啊</P>

letgo508

<>在模具上下摸咬死后開始抽真空,大概20mm左右的位置,這就要求模具本身就有真空管路!</P>

mrfeng

縮小鋪料面積。